Filler and its effect as polymer additves

The term fillers refers to solid polymer additives, which are incorporated into the plastic matrix.

They are generally inorganic materials and can be classified according to their effect on the mechanical properties of the resulting mixture. Inert or extender fillers are added mainly to reduce the cost of the compound, whereas reinforcing fillers are added to improve certain mechanical properties such as modulus or tensile strength.

Although termed inert, inert fillers can nonetheless affect other properties of the compound besides cost. In particular, they may increase the density of the compound, reduce the shrinkage, increase the hardness, and increase the heat deflection temperature. Reinforcing fillers typically will increase the tensile, compressive, and shear strengths, increase the heat deflection temperature, reduce shrinkage, increase the modulus, and improve the creep behavior.

Visit Wadahmakmur Kencana, Polymer Additives Distributor Indonesia.

Reinforcing fillers improve the properties via several mechanisms.

In some cases, a chemical bond is formed between the filler and the polymer; in other cases, the volume occupied by the filler affects the properties of the thermoplastic. As a result, the surface properties and interaction between the filler and the thermoplastic are of great importance. A number of filler properties govern their behavior, including the particle shape, the particle size and distribution of sizes, and the surface chemistry of the particle. In general, the smaller the particle, the greater the improvement in the mechanical property of interest (such as tensile strength).

Larger particles may give reduced properties compared to the pure thermoplastic. Particle shape can also influence the properties. For example, plate-like particles or fibrous particles may be oriented during processing, resulting in anisotropic properties. The surface chemistry of the particle is also important to promote interaction with the polymer and to allow for good interfacial adhesion. The polymer should wet the particle surface and have good interfacial bonding so as to obtain the best property enhancement. Examples of inert or extender fillers include: china clay (kaolin), talc, and calcium carbonate.